The crystal structure of ludwigite from Vranovac ore deposit (Boranja Mt., Serbia) was refined using the X-ray powder diffraction (XRPD) Rietveld method in the space group Pbam to a final RB=7.45% and RF=5.26%. It has the unit cell dimensions of: a=9.2515(2) ?; b=12.3109(2) ?; c=3.03712(7) ?; and V=345.91(1) ?3. The calculated distances and angles are mostly in good agreement with the Mg2+-Fe2+ substitutions across the M(1) and M(3) sites, as well as with the Fe3+-Al3+ replacement in the M(4) site. However, the mean observed M(2)-O distance is considerably shorter than prescribed, due to a slight increase of the Fe3+ content in the M(2) site. Such replacement was compensated by slight increase of the Fe2+ content in the M(4) site, resulting in the (Mg1.48Fe2+0.46Fe3+0.05Mn0.02)2.01(Fe3+0.94Fe2+0.04Al0.02)1.00B1.00O5 composition. The formation temperature was estimated to be about 500–600°C. The influences of the various chemical compositions to the crystallographic parameters, M-O distances, M(3) and M(4) sites shift, distortion parameters and estimated valences, were also studied and compared with other reference samples.